Home>>Technical>>Chemical Composition
Chemical Composition
Grade |
Chemical Compostion |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Others |
304 |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
8.00-11.00 |
18.00-20.00 |
— |
|
304L |
0.035 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
8.00-13.00 |
18.00-20.00 |
— |
|
304N |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
8.00-11.00 |
18.00-20.00 |
— |
N 0.10-0.16 |
304LN |
0.035 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
8.00-11.00 |
18.00-20.00 |
— |
N 0.10-0.16 |
316 |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
10.00-14.00 |
16.00-18.00 |
2.00-3.00 |
|
316L |
0.035 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
10.00-15.00 |
16.00-18.00 |
2.00-3.00 |
|
316N |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
11.00-14.00 |
16.00-18.00 |
2.00-3.00 |
N 0.10-0.16 |
316 LN |
0.035 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
11.00-14.00 |
16.00-18.00 |
2.00-3.00 |
N 0.10-0.16 |
316Ti |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
10.00-14.00 |
16.00-18.00 |
2.00-3.00 |
Ti 5(C+N)-0.70 |
316H |
0.04-0.10 |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
11.00-14.00 |
16.00-18.00 |
2.00-3.00 |
|
321 |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
9.00-13.00 |
17.00-20.00 |
— |
Ti > 5xC, max 0.60% |
317 |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
11.00-14.00 |
18.00-20.00 |
3.00-4.00 |
|
317L |
0.035 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
|
347 |
0.08 max |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
9.00-13.00 |
17.00-20.00 |
… |
Co + Ta > 10xC, max 1.00% |
904L |
0.02 max |
1,0 max |
2,00 max |
0,040 max |
0,030 max |
23.00-28.00 |
19.00-23.00 |
4.00-5.00 |
N ≤ 0.10, Cu 1.0-2.0 |
S31803 |
0.03 max |
1.00 max |
2.00 max |
0.030 max |
0.020 max |
4.50-6.50 |
21.0-23.0 |
2.50-3.50 |
N 0.08-0.20 |
2205 |
0,030 max |
1,0 max |
2,00 max |
0,030 max |
0,020 max |
4.50-6.50 |
22.00-23.00 |
3.00-3.50 |
N 0.14-0.20 |
(S32205) |
405 |
0.08 max |
0.75 max |
1.00 max |
0.040 max |
0.030 max |
0.50 max |
11.50-13.50 |
— |
Al 0.10-0.30 |
410 |
0.15 max |
0.75 max |
1.00 max |
0.040 max |
0.030 max |
0.50 max |
11.50-13.50 |
— |
|
430 |
0.12 max |
0.75 max |
1.00 max |
0.040 max |
0.030 max |
0.50 max |
16.00-18.00 |
— |
|
430Ti |
0.10 max |
1.00 max |
1.00 max |
0.040 max |
0.030 max |
0.75 max |
16.00-19.50 |
— |
Ti 5xC min; 0.75 max |
304H |
0.04-0.10 |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
8.00-11.00 |
18.00-20.00 |
— |
|
321H |
0.04-0.10 |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
9.00-13.00 |
17.00-20.00 |
— |
Ti > 5xC, max 0.60% |
347H |
0.04-0.10 |
0.75 max |
2.00 max |
0.040 max |
0.030 max |
9.00-13.00 |
17.00-20.00 |
— |
Co + Ta > 8xC, max 1.00% |
310S |
0.08 max |
0.75 max |
2.00 max |
0.045 max |
0.030 max |
19.00-22.00 |
24.00-26.00 |
0.75 max |
|
310H |
0.10 max |
1,0 max |
2,00 max |
0,045 max |
0,030 max |
19.00-22.00 |
24.00-26.00 |
— |
|
S32750 |
0.03 max |
0.80 max |
1.20 max |
0.035 max |
0.020 max |
6.00-8.00 |
24.00-26.00 |
3.00-5.00 |
N 0.24-0.35Cu 0.5max |
S32760 |
0.05 max |
1.00max |
1.00 max |
0.030 max |
0.010 max |
6.00-8.00 |
24.00-26.00 |
3.00-4.00 |
N 0.20-0.30Cu 0.5-1.0 |
|